Microstructure and mechanical properties of Al-7.9Zn-2.7Mg-2.0Cu (wt%) alloy strip fabricated by twin roll casting and hot rolling
- Authors
- Zang, Qianhao; Feng, Di; Lee, Yun-Soo; Chen, Hongmei; Kim, Min-Seok; Kim, Hyoung-Wook
- Issue Date
- Dec-2020
- Publisher
- ELSEVIER SCIENCE SA
- Keywords
- Al-Zn-Mg-Cu alloy; Twin roll casting; Microstructure; Second phase; Tensile properties
- Citation
- JOURNAL OF ALLOYS AND COMPOUNDS, v.847
- Journal Title
- JOURNAL OF ALLOYS AND COMPOUNDS
- Volume
- 847
- URI
- https://scholarworks.bwise.kr/gachon/handle/2020.sw.gachon/80183
- DOI
- 10.1016/j.jallcom.2020.156481
- ISSN
- 0925-8388
- Abstract
- High Zn content Al-7.9Zn-2.7Mg-2.0Cu (wt. %) aluminum alloy strip with 5.5 mm thickness was successfully fabricated by twin roll casting (TRC). Fine grain size, second phase and second dendrite arm spacing (SDAS) were obtained in the cast strip due to the high cooling rate during TRC process. Short-time annealing treatment of 480 degrees C-1 h could effectively reduce the second phases, and the elongation of the strip was improved. The TRC alloy sheet with 2.0 mm thickness was fabricated by the annealing treatment (480 degrees C-1 h) and hot rolling. The yield strength, tensile strength and elongation along the rolling direction of the TRC sheet after solution treatment, pre-aging and natural aging were 398 MPa, 590 MPa and 15.74%, respectively. After bake-hardening, the yield strength, tensile strength and elongation along the rolling direction were 550 MPa, 605 MPa and 10.07%, respectively. (C) 2020 Elsevier B.V. All rights reserved.
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - 공과대학 > 신소재공학과 > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholarworks.bwise.kr/gachon/handle/2020.sw.gachon/80183)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.