Synthesis of highly fluorinated poly(arylene ether)s copolymers for proton exchange membrane materials

Abstract

Highly fluorinated poly(arylene ether)s containing sulfonic acid groups meta to ether linkage (SPAE), intended for fuel cell applications as proton electrolyte membrane materials, were synthesized by potassium carbonate mediated nucleophilic polycondensation reactions of commercially available monomers: 2,8-dihydroxynaphthalene-6-sulfonated salt (2,8-DHNS-6), hexafluorobisphenol A (6F-BPA), and decafluorobiphenyl (DFBP) in dimethylsulfoxide (DMSO) at 160-170 degrees C. FT-IR and H-1 NMR were used to characterize the structures. The sulfonate or sulfonic acid contents (SC), expressed as a number per repeat unit of polymer and ranged from 0 to 0.79, were calculated from F-19 NMR. The proton conductivities of acid form membrane increased with SC value and reached 0.103 S/cm at 90 degrees C for SPAE 80. The methanol permeabilities ranged from 7.4 x 10(-7) to 2.2 x 10(-9) cm/s at 30 degrees C and were lower than those of other conventional sulfortated ionomer membranes, particularly commercial perfluorinated sulfonated ionomer (Nation).