Warm compaction of Fe-Si/Fe powder mixture
DC Field | Value | Language |
---|---|---|
dc.contributor.author | 김영도 | - |
dc.date.accessioned | 2021-08-03T23:22:50Z | - |
dc.date.available | 2021-08-03T23:22:50Z | - |
dc.date.issued | 20080824 | - |
dc.identifier.uri | https://scholarworks.bwise.kr/hanyang/handle/2021.sw.hanyang/64072 | - |
dc.description.abstract | 3-D shape Soft magnetic composite parts can be formed by general compaction method of powder metallurgy. In this letter, high density nanostructured Fe-Si/Fe composite prepared by a warm compaction method was presented. Ball-milled Fe-20wt.%Si powder, pure Fe powder and polyvinyl pyrrolidone (PVP) were mixed in acetone solvent and then the powder mixture was compacted at temperature and pressures. Density of samples up to 90% theoretical value has been obtained. The warm compacted sample prepared at 650MPa and 240oC had highest compaction properties in comparison with other compacts at 300, 400MPa and room temperature, 120 and 180oC. | - |
dc.title | Warm compaction of Fe-Si/Fe powder mixture | - |
dc.type | Conference | - |
dc.citation.conferenceName | The Fourth Joint Symposium on Electronic Materials | - |
dc.citation.conferencePlace | Tsukuba, Japan | - |
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.
222, Wangsimni-ro, Seongdong-gu, Seoul, 04763, Korea+82-2-2220-1365
COPYRIGHT © 2021 HANYANG UNIVERSITY.
Certain data included herein are derived from the © Web of Science of Clarivate Analytics. All rights reserved.
You may not copy or re-distribute this material in whole or in part without the prior written consent of Clarivate Analytics.