High-strain-rate solute drag creep in a Cu-22%Sn alloy (Cu17Sn3) with near peritectic composition
- Authors
- Yang, J. Y.; Kim, G. H.; Kim, W. J.
- Issue Date
- Jun-2020
- Publisher
- ELSEVIER SCIENCE INC
- Keywords
- Hot compression; Processing maps; Solute drag creep; Hot workability; Copper alloys; Microstructures
- Citation
- MATERIALS CHARACTERIZATION, v.164
- Journal Title
- MATERIALS CHARACTERIZATION
- Volume
- 164
- URI
- https://scholarworks.bwise.kr/hongik/handle/2020.sw.hongik/11692
- DOI
- 10.1016/j.matchar.2020.110325
- ISSN
- 1044-5803
- Abstract
- Hot compressive deformation behavior and processing maps of the cast Cu-22%Sn alloy with near peritectic composition were examined in the temperature range between 843 and 993 K and in the strain rate range between 10(-3) and 10 s(-1). Solute drag creep associated with a stress exponent of close to 3.5 dominated the plastic flow even at a very high strain rate of 10 s(-1), implying that the Cu-22%Sn alloy with a major phase of beta (Cu17Sn3, disordered body centered cubic) exhibits high-strain-rate solute drag creep. This is a unique property of the Cu-22%Sn alloy because most of the conventional solid-solution alloys exhibit solute drag creep below 10(-3)-10(-2)s(-1). No unstable flow regime appeared in the flow instability maps, and the power dissipation efficiency was high over the entire range of experimental conditions in the power dissipation maps, indicating that the coarse-grained Cu-22%Sn alloy exhibits excellent hot workability at high strain rates. Comparison of the cast Cu-22%Sn alloy with the cast Cu-10%Sn alloy with a single alpha phase (Cu (alpha), face centered cubic) indicates that (1) the flow stress of the Cu-22%Sn alloy is considerably lower than that of the Cu-10%Sn alloy (by a factor of 11) and (2) the onset of significant deviation from solute drag creep is estimated to occur at a considerably higher strain rate (by a factor of 10(5)) in the Cu-22%Sn alloy. Possible explanations on these observations were presented.
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - Graduate School > Materials Science and Engineering > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholarworks.bwise.kr/hongik/handle/2020.sw.hongik/11692)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.