The Effect of Oligomer Blending on the Flow Properties of Polycarbonate
- Authors
- Cho, Sunghwan; Sunmi-Kim; Misuk-Cho; Lee, Youngkwan; Kim, Dongmin; Kim, Whangi
- Issue Date
- Dec-2009
- Publisher
- SPRINGER
- Keywords
- PC; PC oligomer; blend; high flow; viscosity
- Citation
- MACROMOLECULAR RESEARCH, v.17, no.12, pp.1021 - 1024
- Journal Title
- MACROMOLECULAR RESEARCH
- Volume
- 17
- Number
- 12
- Start Page
- 1021
- End Page
- 1024
- URI
- https://scholarworks.bwise.kr/hongik/handle/2020.sw.hongik/21748
- DOI
- 10.1007/BF03218651
- ISSN
- 1598-5032
- Abstract
- We successfully prepared high-flow polycarbonate (PC) by blending commercial PC with a low molecular weight PC oligomer. The oligomer was synthesized by the addition of a large quantity of mono functional phenol groups, and the chain end group was reacted with p-tertiary butyl phenol (PTBP) to block the reactivity. The viscosity average molecular weight (M-v) for the oligomer was about 4,000-5,000 g/mol, compared to similar to 19,000 g/mol for the PC blend obtained by blending 10 wt% of the prepared oligomer with the commercial grade PC (M-v of 2 1,000 g/mol). The blended PC had a melt flow index of 45, which is 2.5 times higher, and a processing temperature that was 20 degrees C lower, than that of commercial grade PC having a similar M-v.
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - ETC > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholarworks.bwise.kr/hongik/handle/2020.sw.hongik/21748)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.