Low-temperature ozone treatment for p-xylene perm-selective MFI type zeolite membranes: Unprecedented revelation of performance-negating cracks larger than 10 nm in polycrystalline membrane structures
- Authors
- Park, Sanha; Lee, Minseong; Hong, Sungwon; Jeong, Yanghwan; Kim, Dongjae; Choi, Nakwon; Nam, Jaewook; Baik, Hionsuck; Choi, Jungkyu
- Issue Date
- Feb-2023
- Publisher
- Elsevier BV
- Keywords
- Zeolite membranes; Grain boundary defect; Crack; Fluorescence confocal optical microscopy; (FCOM); Xylene isomer separation
- Citation
- Journal of Membrane Science, v.668
- Journal Title
- Journal of Membrane Science
- Volume
- 668
- URI
- https://scholarworks.bwise.kr/sch/handle/2021.sw.sch/22536
- DOI
- 10.1016/j.memsci.2022.121212
- ISSN
- 0376-7388
1873-3123
- Abstract
- We report that low-temperature ozone calcination allowed MFI type polycrystalline zeolite membranes to maximize theirp-/o-xylene separation factor (as high as ca. 2000) by suppressing defect formation. Conventional high-temperature calcination and rapid thermal processing, which provide poor and marked p-/o-xylene sepa-ration abilities, respectively, were used for comparison. The corresponding defect structures were quantitatively analyzed by image processing of fluorescence confocal optical microscopy images combined with membrane permeation modeling, revealing the main defects (grain boundary defects and cracks) and their tortuosity, porosity, and size. To the best of our knowledge, we, for the first time, demonstrated that in contrast to common belief, the minor portion of wider cracks instead of the major portion of narrower grain boundary defects determined the final permeation rates. Specifically, the MFI membrane prepared by high-temperature calcination contained many grain boundary defects (narrow; ca. 1 nm) and few cracks (wide; ca. 20 nm) that accounted for ca. 0.1% and 99.8%, respectively, of the slowly permeating o-xylene molar flux. In contrast, the ozone-treated MFI membranes, which only possessed grain boundary defects, achieved the high p-/o-xylene separation per-formance, underlining the need for the selective reduction in the number of wider cracks rather than ubiquitous, narrow grain boundary defects.
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - College of Engineering > Department of Chemical Engineering > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholarworks.bwise.kr/sch/handle/2021.sw.sch/22536)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.