Interfacial reaction and joint reliability of fine-pitch flip-chip solder bump using stencil printing method
- Authors
- Ha, Sang-Su; Kim, Dae-Gon; Kim, Jong-Woong; Yoon, Jeong-Won; Joo, Jin-Ho; Shin, Young-Eui; Jung, Seung-Boo
- Issue Date
- Nov-2007
- Publisher
- ELSEVIER SCIENCE BV
- Keywords
- flip chip; interfacial reaction; stencil printing; bump shear test; joint reliability
- Citation
- MICROELECTRONIC ENGINEERING, v.84, no.11, pp 2640 - 2645
- Pages
- 6
- Journal Title
- MICROELECTRONIC ENGINEERING
- Volume
- 84
- Number
- 11
- Start Page
- 2640
- End Page
- 2645
- URI
- https://scholarworks.bwise.kr/cau/handle/2019.sw.cau/53382
- DOI
- 10.1016/j.mee.2007.05.062
- ISSN
- 0167-9317
1873-5568
- Abstract
- This study was focused on the formation and reliability evaluation of solder joints with different diameters and pitches for flip chip applications. We investigated the interfacial reaction and shear strength between two different solders (Sn-37Pb and Sn-3.0Ag-0.5Cu, in wt.%) and ENIG (Electroless Nickel Immersion Gold) UBM (Under Bump Metallurgy) during multiple reflow. Firstly, we formed the flip chip solder bumps on the Ti/Cu/ENIG metallized Si wafer using a stencil printing method. After reflow, the average solder bump diameters were about 130, 160 and 190 mu m, respectively. After multiple reflows, Ni3Sn4 intermetallic compound (IMC) layer formed at the Sn-37Pb solder/ENIG UBM interface. On the other hand, in the case of Sn-3.0Ag-0.5Cu solder, (Cu,Ni)(6)Sn-5 and (Ni,Cu)(3)Sn-4 IMCs were formed at the interface. The shear force of the Pb-free Sn-3.0Ag-0.5Cu flip chip solder bump was higher than that of the conventional Sn-37Pb flip chip solder bump. (c) 2007 Published by Elsevier B.V.
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - College of Engineering > School of Mechanical Engineering > 1. Journal Articles
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.