대나무 재를 혼합한 플라이에쉬 지오폴리머 콘크리트의 물리적 특성에 대한 연구

Abstract

Malaysia, as a tropical rainforest country, enjoys an abundance of bamboo plant that proliferate throughout the country. The application of geopolymer technology has become a trend and preserve the environment from harm. Fly ash geopolymer concrete has low early strength and requires 24 hours for the concrete to harden. Thus, the presence of calcium and potassium content in bamboo ash could remedy this problem. Besides, there is no research regarding the use of bamboo ash as a binder in geopolymer concrete. Therefore, the presence of bamboo ash could improve the research field with the use of agriculture waste in a building construction. This research aim is to use bamboo ash in the production of fly ash geopolymer concrete. The specimens were casted in 100mm×100mm×100mm 100mm×100mm×100mm cubes and sodium based activator were used as the alkaline solutions. The binders are formulated with different binder ratio. All test specimens were cured at ambient temperature (23∘C−25∘C 23∘C−25∘C ) and 100% fly ash was chosen as control specimen. To determine the mechanical properties of fly sh geopolymer concrete with the presence of bamboo ash, compressive strength test was conducted. The test results depicted that as the percentage of bamboo ash decreases, compressive strength increases. Also, the addition of 5% of bamboo ash into fly ash geopolymer concrete could improve the early strength in 7 days. The results were proven with the result explained by X-ray fluorescence (XRF) and X-ray diffraction (XRD). Therefore, it can be concluded that the addition of bamboo ash improved the properties of fly ash geopolymer concrete at early ages.