Mechanical properties of Si3N4-Al2O3 FGM joints with 15 layers for high-temperature applications
- Authors
- Lee, Sunyong Caroline; Lemberg, Joseph A.; Cho, Danee G.; Roh, Jiyoung; Ritchie, Robert O.
- Issue Date
- May-2010
- Publisher
- Elsevier BV
- Keywords
- Ceramics; Joining; Functionally graded materials; High-temperature strength
- Citation
- Journal of the European Ceramic Society, v.30, no.7, pp.1743 - 1749
- Indexed
- SCIE
SCOPUS
- Journal Title
- Journal of the European Ceramic Society
- Volume
- 30
- Number
- 7
- Start Page
- 1743
- End Page
- 1749
- URI
- https://scholarworks.bwise.kr/erica/handle/2021.sw.erica/39853
- DOI
- 10.1016/j.jeurceramsoc.2010.01.012
- ISSN
- 0955-2219
- Abstract
- "Crack-free" alumina-silicon nitride Joints, comprised of 15 layers of gradually differing compositions of Al2O3/Si3N4, have been fabricated using sialon polytypoids as functionally graded materials (FGM) bonding layers for high-temperature applications Using flexural strength tests conducted both at room and at elevated temperatures, the average fracture strength at room temperature was found to be 437 MPa, significantly, this value was unchanged at temperatures up to 1000 degrees C Scanning electron microscopy (SEM) observations of fracture surfaces indicated the absence of any glassy phase at the triple points This result was (pile contrary to the previously reported 20-layer Al2O3/Si3N4 FGM samples where three-point bend testing revealed a severe strength degradation at high temperatures Consequently, we believe that the Joining of alumina to silicon nitride using polytypoidally functional gradients can markedly improve the suitability of these joints for high-temperature applications. (C) 2010 Elsevier Ltd All rights reserved
- Files in This Item
-
Go to Link
- Appears in
Collections - COLLEGE OF ENGINEERING SCIENCES > DEPARTMENT OF MATERIALS SCIENCE AND CHEMICAL ENGINEERING > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholarworks.bwise.kr/erica/handle/2021.sw.erica/39853)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.