Effects of intermediate metal layer on the properties of Ga-Al doped ZnO/metal/Ga-Al doped ZnO multilayers deposited on polymer substrate

Abstract

Ga-Al doped ZnO/metal/Ga-Al doped ZnO multilayer films were deposited on polyethersulfone (PES) substrate at room temperature. The multilayer films consisted of intermediate Ag metal layers, top and bottom Ga-Al doped ZnO layer. The multilayer with PES substrate had advantages such as low sheet resistance, high optical transmittance in visible range and stable mechanical properties. From the results, sheet resistances of multilayer showed 9 Omega/sq with 12 nm of Ag metal layer thickness. Average optical transmittance of multilayer film showed 84% in visible range (380-770 nm) with 12 nm of Ag metal layer thickness. Moreover the multilayers showed stable mechanical properties than single-layered Ga-Al doped ZnO sample during the bending test due to the existence of ductile Ag metal layer. (C) 2012 Elsevier Ltd. All rights reserved.