Soft Recovery Process of Mechanically Degraded Flexible a-IGZO TFTs With Various Rolling Stresses and Defect Simulation Using TCAD Simulation
- Authors
- Kim, Beom-Su; Jeong, Hyun-Jun; Han, Ki-Lim; Lee, Won-Bum; Kim, Yoon-Seo; Park, Jin-Seong
- Issue Date
- Feb-2020
- Publisher
- IEEE-INST ELECTRICAL ELECTRONICS ENGINEERS INC
- Keywords
- Device reliability; field effect transistors; oxide semiconductor; rolling stress; stress; technology computer-aided design (TCAD) simulation; thin-film transistors (TFTs)
- Citation
- IEEE TRANSACTIONS ON ELECTRON DEVICES, v.67, no.2, pp.535 - 541
- Indexed
- SCIE
SCOPUS
- Journal Title
- IEEE TRANSACTIONS ON ELECTRON DEVICES
- Volume
- 67
- Number
- 2
- Start Page
- 535
- End Page
- 541
- URI
- https://scholarworks.bwise.kr/hanyang/handle/2021.sw.hanyang/10752
- DOI
- 10.1109/TED.2019.2961119
- ISSN
- 0018-9383
- Abstract
- We examine the effects of repetitive rolling stress on thin-film transistors (TFTs) using various rolling radii, and evaluate the subsequent thermal treatment at various temperatures. After applying repetitive rolling stress, the electrical characteristics of the TFTs changes. In particular, change of subthreshold swing (SS) is significant than that of threshold voltage (V-th), and saturation mobilityWe simulated the electrical performance of TFTs using technology computer-aided design (TCAD) to quantitatively ascertain the change to donor-like and acceptor-like defects in the active region. Both Gaussian donor-like defects (N-GD) and acceptor-like defects (N-GA) increased under mechanical strain due to the formation of oxygen-related defects, oxygen vacancy (V-o), and oxygen interstitials (O-i). In addition, negative bias illumination stress (NBIS) reliability results show that degraded TFTs at higher rolling stress yield more variation of threshold voltage and SS due to increase in interface trap site, and defect sites. The rolling stress generates more oxygen-related defects, V-o and O-i, which act as TFT degradation factors. Finally, we investigate the possible recovery mechanism of mechanically degraded TFTs through thermal treatment. Thermal treatment at 150 C and 250 C cannot recover the electrical performance of mechanically stressed TFTs and NBIS reliability to before rolling state. Therefore, we used TCAD simulation to speculate the origin of incomplete recovery. We thought that this incomplete recovery originated from oxygen dimers (O-O) formed from O-i under mechanical stress.
- Files in This Item
-
Go to Link
- Appears in
Collections - 서울 공과대학 > 서울 신소재공학부 > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholarworks.bwise.kr/hanyang/handle/2021.sw.hanyang/10752)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.