RF 열플라즈마를 이용한 Y2O3: Eu 3+ 적색 나노 형광체 분말 합성Synthesis and characterization of Y2O3 : Eu3+ red nano phosphor powders using RF thermal plasma
- Other Titles
- Synthesis and characterization of Y2O3 : Eu3+ red nano phosphor powders using RF thermal plasma
- Authors
- Lee, Seung-Yong; Koo, Sang-Man; Hwang, Kwang-Taek; Kim, Jin-Ho; Han, Kyu-Sung
- Issue Date
- Dec-2015
- Publisher
- KOREAN ASSOC CRYSTAL GROWTH, INC
- Keywords
- Y2O3 : Eu3+ red phosphor; Raw material; RF thermal plasma; Solid state reaction; Photoluminescence
- Citation
- JOURNAL OF THE KOREAN CRYSTAL GROWTH AND CRYSTAL TECHNOLOGY, v.25, no.6, pp.272 - 279
- Indexed
- SCIE
KCI
- Journal Title
- JOURNAL OF THE KOREAN CRYSTAL GROWTH AND CRYSTAL TECHNOLOGY
- Volume
- 25
- Number
- 6
- Start Page
- 272
- End Page
- 279
- URI
- https://scholarworks.bwise.kr/hanyang/handle/2021.sw.hanyang/155791
- DOI
- 10.6111/JKCGCT.2015.25.6.272
- ISSN
- 1225-1429
- Abstract
- Y2O3 : Eu3+는 우수한 적색 발광 특성을 가지고 있는 형광체로 최근 고화질 디스플레이에 대한 수요가 증가함에 따라 관련 연구가 활발히 진행되고 있다. 본 연구에서는 RF 열플라즈마 합성법과 고상법을 이용하여 Y2O3 : Eu3+ 적색 형광체를 합성하였으며, 합성 방법에 따른 Y2O3 : Eu3+ 적색 형광체의 결정 구조, 미세 구조, 발광 특성의 차이를 XRD, TEM, PL 분석을 통해 비교하였다. 고상법으로 합성된 Y2O3 : Eu3+ 적색 형광체의 입자는 약 10~20 μm 크기를 가지는 반면, RF 열플라즈마 합성법을 통해 합성된 적색 형광체는 반응부는 약 100 nm, 필터부는 약 30 nm의 크기를 갖는 나노 형광체로 확인되었다. 합성된 모든 분말들은 PL 측정결과 611 nm(5D0 → 7F2)에서 발광하는 것을 확인하였으며, 결정 크기와 입도가 증가할수록 PL intensity가 증가하였다. 또한, 추가 열처리 공정이 필요 없는 one-step 공정의 RF 열플라즈마 공정을 통해 합성된 Y2O3 : Eu3+ 적색 나노 형광체는 고상법으로 합성된 적색 형광체와 비슷한 발광 특성을 보이는 것을 확인할 수 있었다.
- Files in This Item
-
Go to Link
- Appears in
Collections - 서울 공과대학 > 서울 화학공학과 > 1. Journal Articles
- 서울 공과대학 > 서울 신소재공학부 > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholarworks.bwise.kr/hanyang/handle/2021.sw.hanyang/155791)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.