Preparation of anatase TiO2 thin film by low temperature annealing as an electron transport layer in inverted polymer solar cells
- Authors
- Noh, Hongche; Oh, Seong-Geun; Im, Seung Soon
- Issue Date
- Apr-2015
- Publisher
- ELSEVIER SCIENCE BV
- Keywords
- Inverted polymer solar cell; TiO2 film; Low temperature annealing; PCE; Solvothermal process
- Citation
- APPLIED SURFACE SCIENCE, v.333, pp.157 - 162
- Indexed
- SCIE
SCOPUS
- Journal Title
- APPLIED SURFACE SCIENCE
- Volume
- 333
- Start Page
- 157
- End Page
- 162
- URI
- https://scholarworks.bwise.kr/hanyang/handle/2021.sw.hanyang/157562
- DOI
- 10.1016/j.apsusc.2015.02.010
- ISSN
- 0169-4332
- Abstract
- To prepare the anatase TiO2 thin films on ITO glass, amorphous TiO2 colloidal solution was synthesized through the simple sol-gel method by using titanium (IV) isopropoxide as a precursor. This amorphous TiO2 colloidal solution was spread on ITO glass by spin-coating, then treated at 450 degrees C to obtain anatase TiO2 film (for device A). For other TiO2 films, amorphous TiO2 colloidal solution was treated through solvothermal process at 180 degrees C to obtain anatase TiO2 colloidal solution. This anatase TiO2 colloidal solution was spread on ITO glass by spin coating, and then annealed at 200 degrees C (for device B) and 130 degrees C (for device C), respectively. The average particle size of amorphous TiO2 colloidal solution was about 1.0 nm and that of anatase TiO2 colloidal solution was 10 nm. The thickness of TiO2 films was about 15 nm for all cases. When inverted polymer solar cells were fabricated by using these TiO2 films as an electron transport layer, the device C showed the highest PCE (2.6%) due to the lack of defect, uniformness and high light absorbance of TiO2 films. The result of this study can be applied for the preparation of inverted polymer solar cell using TiO2 films as a buffer layer at low temperature on plastic substrate by roll-to roll process. (C) 2015 Elsevier B.V. All rights reserved.
- Files in This Item
-
Go to Link
- Appears in
Collections - 서울 공과대학 > 서울 화학공학과 > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholarworks.bwise.kr/hanyang/handle/2021.sw.hanyang/157562)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.