Effects of Ga:N Addition on the Electrical Performance of Zinc Tin Oxide Thin Film Transistor by Solution-Processing

Abstract

This paper addressed the effect of gallium nitrate hydrate addition on thin film transistor (TFT) performance and positive bias stability of amorphous zinc tin oxide (ZTO) TFTs by solution processing, Further, the mechanisms responsible for chemical properties and electronic band structure are explored. A broad exothermic peak accompanied by weight loss appeared in the range from about 350 to 570 degrees C for the ZTO solution; the thermal reaction of the Ga-ZTO:N solution was completed at 520 degrees C. This is because the gallium nitrate hydrate precursor promoted the decomposition and dehydroxylation reaction for Zn(CH3COO)(2)center dot 2H(2)O and/or SnCl2 center dot 2H(2)O precursors. The concentrations of carbon and chloride in gallium nitrate hydrate added ZTO films annealed at 400 degrees C have a lower value (C 0.65, Cl 0.65 at. %) compared with those of ZTO films (C 3.15, Cl 0.82 at. %). Absorption bands at 416, 1550, and 1350 cm(-1) I for GaZTO:N films indicated the presence of ZnGa2O4, N-H, and N=O groups by Fourier transform infrared spectroscopy measurement, respectively. As a result, an inverted staggered Ga-ZTO:N TFT exhibited a mobility of 4.84 cm(2) V-1 s(-1) in the saturation region, a subthreshold swing of 0.35 V/decade, and a threshold gate voltage (V-th) of 0.04 V. In addition, the instability of V-th values of the ZTO TFTs under positive bias stress conditions was suppressed by adding Ga and N from 13.6 to 3.17 V, which caused a reduction in the oxygen-related defects located near the conduction band.