Influence of nanopowder characteristics on dispersion property of slurries
- Authors
- Choi, Jinyi; Jung, Younggeul; Kim, Jeonghee; Shin, Dongwook
- Issue Date
- May-2013
- Publisher
- ELSEVIER SCI LTD
- Keywords
- A. Suspensions; D. CeO2; E. Fuel cells
- Citation
- CERAMICS INTERNATIONAL, v.39, pp.S663 - S667
- Indexed
- SCIE
SCOPUS
- Journal Title
- CERAMICS INTERNATIONAL
- Volume
- 39
- Start Page
- S663
- End Page
- S667
- URI
- https://scholarworks.bwise.kr/hanyang/handle/2021.sw.hanyang/162837
- DOI
- 10.1016/j.ceramint.2012.10.157
- ISSN
- 0272-8842
- Abstract
- To investigate the effect of nanopowder characteristics on the slurry properties, the comparative studies on three types of SDC nanopowder synthesized by different methods, i.e., hydrothermal (commercial, SDC I), sol gel (commercial, SDC II) and citric-nitrate combustion (lab-made, SDC III), were carried out. The powder properties were investigated using X-ray diffraction, BET surface area and laser particle size analysis. The slurry stability was confirmed by zeta potential and sedimentation experiments. The samples were similar in the powder sizes, shapes and agglomeration degrees. However, when these samples were dispersed into slurry, the deagglomeration behaviours of particles and dispersion stabilities were significantly different. The powders consist of agglomerates with the average sizes of about 5 mu m; these agglomerates were primary composed of particles with the average size of 20-30 nm. After dispersion, the agglomerates sizes of SDC I, II, and III were reduced to 454.7, 120.5, and 54.8 nm, respectively. The slurry of lab-made SDC nanopowders was the most stable, which resulted from soft agglomeration originated from the nature of synthesis process.
- Files in This Item
-
Go to Link
- Appears in
Collections - 서울 공과대학 > 서울 신소재공학부 > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholarworks.bwise.kr/hanyang/handle/2021.sw.hanyang/162837)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.