Characterization of polymer matrix and low melting point solder for anisotropic conductive film
- Authors
- Eom, Yong-Sung; Baek, Ji-Won; Moon, Jong-Tae; Nam, Jae-Do; Kim, Jong-Min
- Issue Date
- Feb-2008
- Publisher
- ELSEVIER SCIENCE BV
- Keywords
- anisotropic conductive film; low melting point solder; high reliability
- Citation
- MICROELECTRONIC ENGINEERING, v.85, no.2, pp 327 - 331
- Pages
- 5
- Journal Title
- MICROELECTRONIC ENGINEERING
- Volume
- 85
- Number
- 2
- Start Page
- 327
- End Page
- 331
- URI
- https://scholarworks.bwise.kr/cau/handle/2019.sw.cau/23851
- DOI
- 10.1016/j.mee.2007.07.005
- ISSN
- 0167-9317
- Abstract
- The chemo-rheological mechanisms of a polymer matrix and a low melting point solder for an anisotropic conductive film (ACF) have been characterized. For the material characterization of the polymer matrix and solder, a differential scanning calorimetry (DSC) and a dynamic mechanical analyzer (DMA) experiments were conducted. The conversion and viscosity of the polymer matrix was observed by DSC and DMA, respectively. In order to control the curing conditions such as the reaction temperature and time of polymer matrix, the adequate amount of catalyst was used. The compatibility between the viscosity of a polymer matrix and a melting temperature of solder was characterized to optimize the processing cycle. The reductant was also added to remove the oxide layer performed on the surface of solder in the air environment. Based on these chemo-rheological phenomena of the polymer matrix and solder, the optimum polymer system and its processing cycle were designed for the high performance and reliability in the electrical interconnection system. (c) 2007 Elsevier B.V. All rights reserved.
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - College of Engineering > School of Mechanical Engineering > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholarworks.bwise.kr/cau/handle/2019.sw.cau/23851)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.