일방향 및 직교형 유리섬유/에폭시 복합재로 피막된 판유리의 미소강구 충격에 의한 표면파괴거동Surface Fracture Behaviors of Unidirectional and Cross Ply Glass Fiber/Epoxy Lamina-Coated Glass Plates under a Small-Diameter Steel Ball Impact
- Other Titles
- Surface Fracture Behaviors of Unidirectional and Cross Ply Glass Fiber/Epoxy Lamina-Coated Glass Plates under a Small-Diameter Steel Ball Impact
- Issue Date
- Aug-2009
- Publisher
- 한국복합재료학회
- Keywords
- 복합재피막 판유리; 미소강구충격; 섬유배향효과; 표면파괴지수; composite layer-coated glass plate; small steel ball impact; fiber orientation effects; surface fracture index
- Citation
- Composites Research, v.22, no.4, pp.33 - 40
- Indexed
- KCI
- Journal Title
- Composites Research
- Volume
- 22
- Number
- 4
- Start Page
- 33
- End Page
- 40
- ISSN
- 2288-2103
- Abstract
- 유리섬유/에폭시 복합재료로 피막한 판유리의 표면파괴거동에 대한 섬유방향효과를 미소강구 충격실험을 통해 연구했다. 본 연구에서는 단순소다유리판(soda-lime glass plates), 일방향 유리섬유/에폭시박막 (glass/epoxy lamina ply)을 1층 및 2층 접착, 직교형 유리섬유/에폭시 박막 (2층)을 접착한 4종류의 시편을 사용하였다. 유리판 배면에 스트레인게이지를 부착하여 충격중의 최대 응력과 흡수파괴에너지를 측정하였다. 피막없는 판유리의 경우 충격속도 증가에 따라 링균열, 콘균열, 레이디얼 균열이 충격표면부에서 발생하였다. 복합재료 박막으로 피막한 결과, 소다유리판의 균열은 현저히 감소하였으며 섬유층과 판유리 사이의 박리 및 소성변형영역의 방향은 섬유방향으로 진행했다. 최대응력과 흡수파괴에너지를 이용하여 구한 충격 표면파괴지수는 표면저항의 효과적인 평가지수로서 사용될 수 있었다.