경화된 하이드로탈사이트 혼입 포틀랜드 시멘트 페이스트의 염소이온 고정능력 평가

Abstract

Deterioration of reinforced concrete structures due to salt corrosion is a phenomenon that can be easily seen, and the main reason for deterioration is chloride ion. Therefore, researches are actively conducted to control chlorine ion penetration worldwide. The purpose of this study is to evaluate the chloride ion fixation capacity of Portland cement paste containing Hydrotalcite. For this purpose, cement paste containing 0%, 2.5%, and 5% of Hydrotalcite was sealed and cured for 28 days, and the cured cement paste was crushed. Chloride ion solution was prepared at a concentration of 0.5M using NaCl, and the powdered cement paste was reacted for a specific time in aqueous chloride ion solution. After the reaction, the concentration of the chloride ion aqueous solution was measured using a silver nitrate potentiometric titrator, and the reacted cement paste was analyzed using XRD and FT-IR.