Effects of Post Annealing Temperatures on Sputtered Indium Tin Oxide Films for the Application to Resistive Touch Panel
- Authors
- Lee, Soo Min; Lee, Jeong Min; Kwon, Sang Jik; Cho, Eou Sik
- Issue Date
- 1-Jan-2013
- Publisher
- TAYLOR & FRANCIS LTD
- Keywords
- Indium tin oxide (ITO); in-line DC sputtering; linearity; post-annealing; resistive touch panel
- Citation
- MOLECULAR CRYSTALS AND LIQUID CRYSTALS, v.586, no.1, pp.138 - 146
- Journal Title
- MOLECULAR CRYSTALS AND LIQUID CRYSTALS
- Volume
- 586
- Number
- 1
- Start Page
- 138
- End Page
- 146
- URI
- https://scholarworks.bwise.kr/gachon/handle/2020.sw.gachon/14817
- DOI
- 10.1080/15421406.2013.853510
- ISSN
- 1542-1406
- Abstract
- Indium tin oxide (ITO) films were deposited on glass substrates by in-line DC sputtering and were annealed at different temperatures in the main chamber of sputter. The post-annealing effects on the optical and electrical properties of the ITO films were investigated and analyzed by various measurement systems. The results show that a higher annealing temperature makes an improvement on the electro-optical properties of the ITO films. The resistivity of the ITO films was reduced from 8.90x10(-4)cm to 2.91x10(-4)cm and the transmittance was increased from about 76.91% to 82.15% after post annealing at 300 degrees C in vacuum. The post annealed ITO glass was used in the fabrication of resistive touch panel and it was possible to obtain the better linearity characteristics than those from the touch panel fabricated with non-annealed ITO glass.
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - IT융합대학 > 전자공학과 > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholarworks.bwise.kr/gachon/handle/2020.sw.gachon/14817)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.